#1
|
|||
|
|||
Coloring titanium
If you are bored at your shining titanium turnbuckles, you could color them easily at home
It's all about voltage. The cheapest way is to color them gold. All you need is 12V DC, like all we have to drive the chargers. Apart of that you need baking soda and water Look at my video and you will see how easy it is, even if you don't understand the language http://www.youtube.com/watch?v=oh-4F...1&feature=plcp |
#2
|
||||
|
||||
That looks great and fast too. What is the metal used as the cathode ?
__________________
My feedback http://www.oople.com/forums/showthread.php?t=19395 |
#3
|
|||
|
|||
coloring titanium
Very, very impressive !!!
Do you think it could also work with steel ? congrat |
#4
|
||||
|
||||
I would use lead for the cathode as for doing other metals. anodising is what you are doing here so aluminum can also be done however it must be done in sulphuric acid and you have to use a dye aswell to get the colour
titanium is differnt as the colour is dependent on voltage
__________________
DO NOT BUY/SELL TO THIS USER. |
#6
|
||||
|
||||
i want red turnbuckles now
|
#7
|
|||
|
|||
|
#8
|
||||
|
||||
How could I manage to get blue onse like the Associated ones?
__________________
|
#10
|
||||
|
||||
A search on youtube was usefull.
If you are going to do this to quite a few parts and want to get a consistant colour then you are going to need a regulated DC power supply and take note of the voltage for the colour you want.
__________________
My feedback http://www.oople.com/forums/showthread.php?t=19395 |
#11
|
||||
|
||||
I Posted about this last year!
Not one reply Use sugar soap for the electrolyte
__________________
|
#12
|
|||
|
|||
Does it hold it's colour?
Does the colour oxidise and fade like the colours you get when you heat titanium?
-Joolstacho |
#13
|
||||
|
||||
N e body fancy doing mine for me?